Melting Point, °C

174-180

Specific Gravity

1.01

Tensile Strength at Break, MPa

56-69

Tensile Elongation at Break, %

250-390

Flexural Modulus, MPa

1100-1260

Hardness, Shore D

68-72

Charpy Impact, kJ/m²
Notched
23° C
-30° C

5-15
5-8

Example Grades

AESN P202 Blk T6LD
AESNO P10 TL
AESN P210 Blk TL

Melting Point, °C

171-178

Specific Gravity

1.02-1.03

Tensile Strength at Break, MPa

49-58

Tensile Elongation at Break, %

250-370

Flexural Modulus, MPa

390-550

Hardness, Shore D

61-64

Charpy Impact, kJ/m²
Notched
23° C
-30° C

14-NC
3-7

Example Grades

AESNO P40
AESNO P40 TL
AESN P40 Blk TL
AMNO P40 TL

Melting Point, °C

168-176

Specific Gravity

1.01-1.04

Tensile Strength at Break, MPa

50-56

Tensile Elongation at Break, %

300-340

Flexural Modulus, MPa

360-400

Hardness, Shore D

61-64

Charpy Impact, kJ/m²
Notched
23° C
-30° C

25-NC
4-5

Example Grades

AZM 23 T6LD
AZM 30 Blk T6LD

Melting Point, °C

174-181

Specific Gravity

1.01-1.41

Tensile Strength at Break, MPa

72-145

Tensile Elongation at Break, %

4-8

Flexural Modulus, MPa

3000-9000

Hardness, Shore D

70-80

Charpy Impact, kJ/m²
Notched
23° C
-30° C

10-23
7-17

Example Grades

ASR 13

Melting Point, °C

174-178

Specific Gravity

1.2-1.4

Tensile Strength at Break, MPa

37-50

Tensile Elongation at Break, %

30-40

Flexural Modulus, MPa

1750-2000

Hardness, Shore D

Charpy Impact, kJ/m²
Notched
23° C
-30° C

5-6
4-5

Example Grades

AESN Blk P212 CTL

Melting Point, °C

176-178

Specific Gravity

1.14

Tensile Strength at Break, MPa

39

Tensile Elongation at Break, %

180-190

Flexural Modulus, MPa

740

Hardness, Shore D

71

Charpy Impact, kJ/m²
Notched
23° C
-30° C

45
7

Surface resistivity, kOhm

<100

<100